Product Description

Fabric-Bond 24 Epoxy Adhesive Strongest Bonding Agent 24 hour Adhesion

PRODUCT DESCRIPTION:

Fabric-Bond is a two part, heat-resistant and low exotherm, epoxy adhesive formulation. It is a 100% solid epoxy adhesive, with superior chemical resistance and shear strength.

Leather-Bond contains a thixotrophic agent which impedes thinning out of the material during heat cure when properly mixed and cured.

GENERAL PROPERTIES

Appearance	Amber
Cure Type	Room temperature or Heat Cure
Benefits	Room temperature or Heat Cure Tough enamel like cure Bonds to a variety of substrates Weather resistant
Mix Ratio by weight	100:100 / Resin:Hardener
Substrates	Leathers, glass, ceramics, wood and many plastics
Operating Temperature	-60 to 163 C
Typical Application(s)	Staking components, bonding, laminating and repair applications

UNCURED PROPERTIES:

Specific Gravity, mixed	1.07
Reactive solids contents, %	100
Pot Life	60 minutes

CURE SCHEDULE:

4 to 6 hours	@ 65C
24 hours	@ 25C

MISC PROPERTIES:

Shelf Life	2 years closed packaging
Glass Transition Temp, Tg	93C
Hardness, Shore D	78
Lap shear	2900 psi (Alum to Alum)

GENERAL INFORMATION:

For safe handling information on this product, consult the Material Safety Data Sheet, (MSDS).

HOW TO USE:

1) Carefully clean and dry all surfaces to be bonded.

2) Apply Leather-Bond completely mixed adhesive to the prepared surfaces, and gently press these surfaces together. Contact pressure is adequate for strong, reliable bonds; however, maintain contact until adhesive is completely cured.

3) Some separation of components is common during shipping and storage. For this reason, it is recommended that the contents of the shipping container be thoroughly mixed prior to use.

4) Some ingredients in this formulation provided may crystallize when subjected to low temperature storage. A gentle warming cycle of 52C for 30 minutes prior to mixing components may be necessary. Crystallized epoxy components do not react as well as liquid components and should be re-dissolved prior to use for best results.

AVAILABILITY:

This epoxy can be supplied in various different packages.